三氧化钼纳米带电致变色过程中的缺陷变化研究

三氧化钼纳米带电致变色过程中的缺陷变化研究摘要：三氧化钼是一种重要的光电功能材料，已在很多领域得到应用。本文研究三氧化钼纳米带电致变色过程中缺陷的变化。通过合成不同尺寸的三氧化钼纳米带并对其进行光学和

三氧化钼纳米带电致变色过程中的缺陷变化研究 摘要： 三氧化钼是一种重要的光电功能材料，已在很多领域得到应用。本 文研究三氧化钼纳米带电致变色过程中缺陷的变化。通过合成不同尺寸 的三氧化钼纳米带并对其进行光学和电学测试，发现在光激发下，三氧 化钼纳米带经历了一个电致变色过程，同时缺陷密度也发生了明显的变 化。通过进一步的分析，我们认为这是由于电子的激发和迁移导致了缺 陷的形成和消失。 关键词：三氧化钼，纳米带，电致变色，缺陷。 Abstract: Molybdenum trioxide is an important optoelectronic functional material that has been widely used in many fields. This study investigates the changes in defects during the color change induced by electric charge in molybdenum trioxide nanoribbons. By synthesizing different sizes of molybdenum trioxide nanoribbons and conducting optical and electrical tests on them, it was found that under light excitation, molybdenum trioxide nanoribbons undergo an electrically induced color change process, while the defect density also undergoes significant changes. Through further analysis, it is believed that this is due to the excitation and migration of electrons leading to the formation and disappearance of defects. Keywords: molybdenum trioxide, nanoribbon, electrically induced color change, defect. 引言： MoO3 三氧化钼（）是一种重要的功能材料，因其在光电领域的优异 [1] 性能已成为当前研究的热点之一。纳米级别的三氧化钼材料由于其独 特的表面性质而具有特殊的光电性质，尤其是其纳米带形态的三氧化钼 具有在可见光区域的高透过率和较小的折射率，这对于相关领域中的传 [2,3] 感器、透明导电膜和光电器件的应用具有重要的意义。除此之外， 三氧化钼纳米带还表现出了电致变色的特性，这种特性与其缺陷密度的